Preparation of 3D printed silicon nitride bioceramics by microwave sintering | Scientific Reports

Nov 13, 2024

Scientific Reports volume 14, Article number: 15825 (2024) Cite this article

727 Accesses

Metrics details

Silicon nitride (Si3N4) is a bioceramic material with potential applications. Customization and high reliability are the foundation for the widespread application of Si3N4 bioceramics. This study constructed a new microwave heating structure and successfully prepared 3D printed dense Si3N4 materials, overcoming the adverse effects of a large amount of 3D printed organic forming agents on degreasing and sintering processes, further improving the comprehensive performance of Si3N4 materials. Compared with control materials, the 3D printed Si3N4 materials by microwave sintering have the best mechanical performance: bending strength is 928 MPa, fracture toughness is 9.61 MPa·m1/2. Meanwhile, it has the best biocompatibility and antibacterial properties, and cells exhibit the best activity on the material surface. Research has shown that the excellent mechanical performance and biological activity of materials are mainly related to the high-quality degreasing, high cleanliness sintering environment, and high-quality liquid-phase sintering of materials in microwave environments.

Silicon nitride (Si3N4) is a non oxide ceramic that has been widely used in industry and has been studied for its use in the biomedical field since 19891,2,3,4,5,6,7,8,9,10,11,12,13. The basic theory of using silicon nitride implant in the biomedical field is based on its excellent combination of mechanical performance, microstructure, and biological activity4,6,8. Porous silicon nitride implants have shown exciting results in the maxillofacial and spinal surgery5,8. However, Si3N4 material has high vickers hardness up to 15 GPa2, is not easy to process, has high customization costs, and a long preparation time cycle, so its market application is very limited. In addition, due to the high sintering temperature of Si3N4 materials, traditional sintering preparation methods such as gas pressure sintering (GPS) and hot press sintering (HPS) are influenced by various complex factors such as graphite atmosphere, heating environment, heat transfer mechanism, and high-temperature decomposition of Si3N414,15. Its mechanical properties have not reached the ideal level, and its biocompatibility still fluctuates6. If the mechanical performance and biological activity of Si3N4 materials are further improved, the implants have great potential for application in areas that urgently need improvement, such as the heart and skull11. The performance of Si3N4 bioceramic materials still needs further improvement and verification.

Three-dimensional (3D) printing technology is an emerging digital model-based manufacturing technology that achieves object preparation through layer by layer construction. The 3D technology stands out for cost-effectiveness, adjustable speed for any design flexibility, positioning itself. It is a cutting-edge hot spot in the study of advanced material forming and preparation technology. It has great potential for application in the field of inorganic non-metallic materials16,17,18,19,20,21,22. In recent research, 3D printing can solve the problem of customizing silicon nitride bioceramic materials12,21,23. However, the organic content of 3D printing slurry is high, with DLP resin content exceeding 50 vol%21,23 and FDM organic content also reaching 47 vol%9,12, which is prone to defects such as degreasing, cracking, and low sintering density. This is currently a major bottleneck problem hindering the preparation of dense silicon nitride bioceramics by 3D printing.

Microwave sintering (MS) is a method of achieving densification by coupling the special wavelength band of microwave with the basic microstructure of materials to generate heat, and the dielectric loss of materials heats them up to the sintering temperature as a whole. It is an efficient and energy-saving sintering method, which has many advantages such as selective self-heating, uniform and rapid heating, reduced sintering temperature, and no pollution24,25,26,27,28,29. If it is applied to the preparation of Si3N4 materials, it is of great significance to improve the degreasing effect, production efficiency, sintering environment of Si3N4 materials, reduce the sintering temperature of Si3N4, inhibit the decomposition of Si3N4, and improve the mechanical performance and biological activity of the Si3N4 materials. However, due to the poor absorption performance of Si3N4 materials, they cannot be effectively heated quickly, and the high sintering temperature of Si3N4 materials makes it impossible for sintered insulation materials to directly withstand its temperature30,31. Therefore, a new MS structures suitable for degreasing and sintering of Si3N4 urgently need to be established. In recent years, there are few research reports on microwave sintering of dense Si3N4 materials.

This research prepared dense Si3N4 bioceramics using fused deposition molding (FDM) printing method, microwave rapid degreasing and sintering method. Their mechanical performance and biological activity were tested, and compared with GPS Si3N4, and HPS Si3N4, Alumina, Titanium alloy, and PEEK. The influence of microwave heating method on the rapid and safe degreasing, crystal structure growth, mechanical performance, and biocompatibility of 3D printed silicon nitride materials were discussed, and their mechanisms were simulated and explained. Finally, positive and feasible results were obtained for the application of microwave sintered 3D printed dense silicon nitride bioceramic materials in the biomedical field.

The preparation process of 3D printed Si3N4 bioceramics was shown in Fig. 1a. Similar to previous research12, the raw material used in this study was Si3N4 powder (Ube, SN-E10, Japan, D50 = 0.65 μm, SBET = 8.7 m2/g), with Y2O3, CeO2, and MgO as sintering aids. Mix ceramic powder and organic adhesives (polyethylene, paraffin, ethylene vinyl acetate copolymer, stearic acid) in a double roller mixer at a mixing temperature of 150–170 °C for 55 min to form a slurry. The overall volume fraction of ceramic powder in the slurry is 53%. 3D test samples were prepared and printed using a screw extrusion FDM printer (UP-R200, Shenzhen Shenghua 3D Technology Co., Ltd.). The 3D test samples were prepared in strip shape of 50 mm × 6 mm × 4 mm and circular shape with dimension of Φ13 mm × 4 mm using a “single line” filling path. The printed samples degreased in a 45 °C kerosene solvent for 24 h, and then dried it in a 45 °C hot air oven for 16 h.

(a) Preparation process of 3D printed Si3N4 bioceramics samples; (b) The new MS structure diagram constructed in this research.

The next program is degreasing, with the aim of safely removing large amounts of organic matter from 3D printed samples. For the preparation of GPS and HPS samples, in order to reliably degrease the samples, the dried bodies were placed in a hot degreasing furnace and heated in the air at a heating rate of 1 °C/min to 600 °C. During the degreasing process, the samples were kept at 200 °C for 1 h, followed by 300 °C for 2 h, and lastly 600 °C for 3 h, respectively. For the GPS method, the hot degreased bodies were placed in a gas pressure sintering furnace (5518, 6 MPa, Xiangtan Xinyun Technology Co., Ltd.) and heated to 1700 °C at a heating rate of 2 °C/min under nitrogen pressure of 1.8 MPa, with insulation for 2.5 h. For the HPS method, the hot degreased bodies were placed in a hot press sintering furnace (1800 °C, 25 MPa, Hunan Jinteke Technology Co., Ltd.) and heated to 1650 °C at a heating rate of 5 °C/min under nitrogen atmosphere (atmospheric pressure) and a mechanical pressure of 18 MPa, with insulation for 2.5 h.

For the MS method, the dried bodies were placed in a gas microwave sintering furnace (2.45 GHz, 6 kW, Hunan Huaye Microwave Technology Co., Ltd.). Firstly, microwave heating degreasing was carried out in the air at a heating rate of 5 °C/min to 600 °C, followed by insulation at 200 °C for 15 min, 300 °C for 30 min, and 600 °C for 30 min. Then, gas was replaced (microwave heating was suspended), and heating was continued at a heating rate of 5 °C/min under a nitrogen atmosphere (atmospheric pressure) to 1620 °C, with insulation for 1 h. The new MS structure is shown in Fig. 1b. The system consists of four 1.5 kW 2.45 GHz microwave sources and two ceramic (Alumina) tubes. The outer ceramic tube was inserted into the cavity and surrounded by alumina ceramic fiber blocks. The internal ceramic tube was inserted into the outer one. Fill high-purity alumina hollow balls between the inner and outer alumina ceramic tubes. The materials were placed inside the internal ceramic tube and putted on the SiC susceptor. Due to the combination of double alumina tube and high-purity alumina hollow ball structure, the system was capable of achieving temperatures above 1600 °C within a short time, and maintain the high temperature for a longer period of time.

After sintering, the bioceramics samples were ground using diamond grinding tool (Diamond particles of 180 mesh) to produce strip shaped (3 mm × 4 mm × 36 mm) and circular (Φ10 × 3 mm) specimens with a surface finish of 0.6 μm. The control material samples with the same specifications include Alumina (99%, Foshan Haocai New Material Technology Co., Ltd.), Titanium alloy (CT4, Hebei Bo Titanium Metal Materials Co., Ltd.), and PEEK (Faint yellow, Shenzhen Caocheng Plastic Materials Co., Ltd.).

The density of both treated samples was measured by the Archimedes drainage method. Vickers hardness of samples was measured by using a hardness tester, applying a test force of 98.1 N (10 kg) to materials using an indenter, and holding it for 15 s to obtain hardness data. The three-point bending strength and compressive strength of the long strip specimen were tested with a universal material testing machine (Instron Model 5928, USA). The elastic modulus is calculated by formula (1) (ICS 81. 060. 20: Q 32):

P1 and P2 are the initial and final loads of the material loaded within a linear range, respectively. L is the distance between the sample supports, b is the width of the sample, h is the thickness of the sample, and ε1 and ε2 are the strain at the mid span of the sample corresponding to P1 and P2, respectively. The variables on the formula (1) can be measured by the universal material testing machine (Instron Model 5928, USA). The fracture toughness of samples was tested using the method of unilateral pre-cracking. SEM (TESCAN Bmo, s.r.o., TESCAN MIRA, Brno, Czech Republic) was used to observe the microstructure of Si3N4 bioceramics samples. Samples phase analysis was performed by XRD (40 kV, 40 mA, D/MAX-RBX, Rigaku, Osaka, Japan), with a scanning speed of 5°/min and a scanning range of 5–80°.

Take MC3T3-E1 cells (Wuhan Pricella Biotechnology Co., Ltd., Hubei, China) cultured to the third generation, digest with 0.25% trypsin, and resuspend evenly α In MEM culture medium, adjust the cell concentration to 3 × 104/mL using a blood cell counting plate. Place the material sample in a culture dish, inoculate the above cell suspension for in vitro cell culture, and culture it in a 37 °C incubator. At three time points on the 1st, 3rd, and 5th days, discard the original culture medium, add CCK-8 reagent and culture medium, place them in the dark environment to incubate for 2 h, and take them out. Use a fully automatic multifunctional microplate reader (Biotek Instruments.Inc Epoch™) to measure the absorbance value (OD value) of each well at 450 nm for the culture medium containing CCK-8 in the culture dish, and collect the detection data.

Antibacterial properties of samples against Staphylococcus aureus (S. aureus, Beijing Biobw Biotechnology Co., Ltd., Beijing, China) and E. coli (E. coli, Beijing Biobw Biotechnology Co., Ltd., Beijing, China) were determined by colony count method. Luria Bertani broth was used for culturing S. aureus (ATCC 25,923) and E. coli (ATCC 25,922). The microbiological culture was inoculated to the sample specimen and incubate at 37 °C for 24 h. A certain amount of PBS was used to strongly clean the sample and separate microorganisms from the material. Sterilized PBS was used to dilute the eluent. A total of 100 μL of diluted eluent was added to LB broth agar medium. This was then incubated at 37 °C for 24 h, and the number of colonies counted.

MC3T3-E1 cells were seeded on the discs at a density of 4 × 104 cells per well in 24-well plates and cultured for 1 day. The samples were then stained with 2-(4-Amidinophenyl)-6-indole-

-carbamidine dihydrochloride (DAPI, Beyotime Biotech, Shanghai, China) and Actin-Tracker Red-Rhodamine (Beyotime Biotech, Shanghai, China) to observe the cell morphology using confocal laser scanning microscope (CLSM, Zessi, LSM800, Oberkochen, Germany). The morphology of the adhered cells on the discs was also observed by SEM (TESCAN Bmo, s.r.o., TESCAN MIRA, Brno, Czech Republic) after dehydrating the samples in gradient ethanol solutions (30, 50, 70, 85, 90, and 100%, respectively) for 10 min and drying at the critical point.

Each experiment was repeated three times for statistical analysis. The mean ± standard deviation is used to represent the experimental results. Use statistical product and service solution 26.0 software (SPSS 26.0, IBM, New York, USA) to conduct student one-way analysis of variance (ANOVA) on the data *P < 0.05 indicates statistical significance.

The 3D printed Si3N4 billet prepared in this study contains a large amount of organic matter. The TG-DSC curve in the air atmosphere is shown in the Fig. 2a. It can be seen that the significant weightlessness starts from above 200 °C and ends completely at around 600 °C. The total weight of the billet has been reduced to 78.17%, which is consistent with the solid content of the slurry. So, the mixing temperature of slurry in this research is suitable from 150 to 170 °C, and the mixing operation within this temperature range will not affect the organic matter content in the printed material. And the organic matter can be completely removed by holding at 600 °C for 3 h. In addition, a significant exothermic peak appeared after 390 °C, which was caused by the further exothermic reaction between the residual carbon generated after organic matter cracking and oxygen in the air. These residual carbons contribute to the absorption of microwaves for auxiliary heating at 400– 500 °C in this study, achieving uniform heating.

(a) The TG-DSC curve of 3D printed Si3N4 body; (b) The heating curves of 3D printed MS, GPS, and HPS Si3N4 samples; (c) Comparison of XRD between 3D printed MS, GPS and HPS samples, all peaks correspond to those of a reference β-Si3N4 (JCPDS 33-1160).

Figure 2b shows the heating curves of 3D printed MS, GPS, and HPS Si3N4 samples. Although there is a large amount of organic matter in the 3D printed Si3N4 body, due to the characteristics of microwave heating, the material itself absorbs microwave energy for heating. The MS curve has a fast-heating speed, short insulation time, high efficiency, and does not require equipment replacement, allowing for continuous degreasing and sintering. However, GPS and HPS equipment cannot be heated to 600 °C in the air to remove residual carbon due to their graphite heating element and carbon insulation materials. Therefore, degreasing and sintering need to be carried out in different equipment. In addition, due to the fact that the degreasing furnace also belongs to radiation heating, the heating uniformity is poor, and the removal of a large amount of organic matter requires slow degreasing. It is also important to note that the low strength green body after degreasing needs to be carefully transported, otherwise it may cause damage during transportation, resulting in a significant decrease in preparation efficiency.

Figure 2c shows the XRD of 3D printed MS, GPS and HPS Si3N4 samples. Figure 2c evidences that the α-Si3N4 crystal phase has completed transformation and transformed into β-Si3N4 after densification sintering for samples of MS Si3N4, GPS Si3N4, or HPS Si3N4. The main characteristic peaks of β-Si3N4 at 2θ = 27.2°, 33.8°, and 36.2° appear in the XRD spectra, and all peaks correspond to those of the reference β-Si3N4 (JCPDS 33-1160). Due to the Y2O3-CeO2-MgO sintering aid system, the temperature point at which liquid phase appears in silicon nitride materials is approximately 1500 °C32,33. In this research, the higher sintering temperatures resulted in more pronounced liquid phase effects and more complete crystal growth12. Moreover, at the high temperatures, sintering aids gradually evaporate or exist in the silicon nitride lattice, resulting in no relevant crystal phase display in XRD34,35.

To further study the mechanism of material action, SEM microscopic morphology analysis was conducted on the surface of the 3D printed Si3N4 sample of MS, GPS, HPS, as shown in Fig. 3. As shown in Fig. 3a, b, the crystal boundaries of the GPS Si3N4 sample are not very clear, with a small number of impurities between the grain boundaries. The crystal growth is incomplete, and the crystal shape is basically long columnar, but there are many connected crystals, indicating that there is still residual liquid phase. The crystal diameter is relatively large, with a typical crystal diameter of 0.6–0.8 μm and a small aspect ratio of about 3– 5. As shown in Fig. 3c, d, the crystal boundaries of the HPS Si3N4 sample are not clear. There are many impurities between the grain boundaries. The crystal growth is incomplete, and the crystal shape is irregular, making it difficult to distinguish obvious long columnar crystals. The connection between the crystals is severe, indicating that there is still a large residual liquid phase. The crystal size is relatively large, with a typical crystal diameter of 1.0–2.0 μm. Because the crystals are basically in an intersecting state, the aspect ratio cannot be estimated. From Fig. 3e, f, it can be seen that the crystal boundaries of MS Si3N4 sample are clear. There are basically no residual liquid impurities between the grain boundaries. The crystal growth is complete, with clear diamond angles and a regular crystal shape of long columnar crystals. The crystal diameter is small, with a typical crystal diameter of 0.4–0.6 μm and a large aspect ratio of about 5–10. Compared with MS sintering technology, in the case of GPS and HPS sintering technology, there are obvious impurities in the silicon nitride grain boundaries. These impurities are high-temperature liquid phase substances generated by the joint action of silicon nitride materials and additives during the sintering process9,14. These high-temperature liquid phase substances play a crucial role in the transformation of silicon nitride crystal phase at high temperatures. After the completion of the transformation, they are ultimately retained in the silicon nitride grain boundaries due to the influence of sintering methods or the degree of liquid phase action. These grain boundary phase substances are brittle and have a significant negative impact on the mechanical properties of silicon nitride sintered materials9,14,15. From the microstructure shown in Fig. 3, different fracture modes can also be observed, indicating significant differences in crystal integrity and strength of silicon nitride materials under different sintering methods. After the GPS sample fractures, it basically presents a relatively complete crystal morphology. Although there is a small amount of liquid phase adhesion, the crystal strength is high and not easily damaged; After the fracture of the HPS sample, it basically presents a crystal damage morphology, with a lot of liquid phase substances at the grain boundaries, resulting in abnormal crystal growth and high brittleness14,15; After the MS sample fractures, it presents a complete crystal morphology with almost no liquid phase material in the grain boundaries. The crystal has high strength and is not easily damaged. This material relies on the intersection of intact crystals to achieve high mechanical strength12.

Microscopic morphology of the 3D printed MS, GPS and HPS samples. (a) The surface SEM of GPS Si3N4 (5.0 kx); (b) The surface SEM of GPS Si3N4 (10.0 kx); (c) The surface SEM of HPS Si3N4 (5.0 kx); (d) The surface SEM of HPS Si3N4 (10.0 kx); (e) The surface SEM of MS Si3N4 (5.0 kx); (f) The surface SEM of MS Si3N4 (10.0 kx).

Table 1 shows the comparison of mechanical performance between 3D printed Si3N4 samples with different sintering method and Al2O3, Ti-alloy, PEEK, and Cortical bone. As shown in Table 1, the density of MS Si3N4 sample is slightly lower than that of GPS Si3N4 samples and HPS Si3N4 samples, but the difference is not significant, with an average density of 3.23 g·cm−3, which is at an intermediate level compared to other comparative materials. In terms of elastic modulus, MS Si3N4 sample is not significantly different from GPS Si3N4 and HPS Si3N4, and belongs to the intermediate level compared to other comparative materials. The MS Si3N4 samples exhibits exllent mechanical performance: bending strength is 928 MPa, fracture toughness is 9.61 MPa·m1/2, vickers hardness is 16.2 GPa, compressive strength is 3215 MPa. There are also significant advantages compared to the other materials: Ti-alloy, Al2O3, PEEK, and Cortical bone.

The cytotoxicity test results of MS Si3N4, GPS Si3N4 and HPS Si3N4 are shown in Fig. 4. During the cell culture time, cells can grow normally on different sintering processes of Si3N4 bioceramics and control samples, and the cell viability on Si3N4 sample is obviously higher than that on the control materials such as Al2O3, Ti-alloy, and PEEK. The difference in cytotoxicity of Si3N4 samples prepared by different sintering processes is not significant. From the results data, the OD450 value of MS Si3N4 is 3.51, the OD450 value of HPS Si3N4 is 3.40, and the OD450 value of GPS Si3N4 is 3.44. The larger the OD450 value, the lower its cytotoxicity. Therefore, in terms of cytotoxicity, MS Si3N4 < GPS Si3N4 < HPS Si3N4. The results indicate that the Si3N4 sample prepared by MS process has the lowest cytotoxicity.

Comparison of cytotoxicity between 3D printed Si3N4 samples with different sintering method and Al2O3, Ti-alloy, PEEK.

The antibacterial effects of Si3N4 samples prepared by different sintering processes and control samples on E. coli are shown in Fig. 5a–g. The bacterial count of corresponding flat plates for Al2O3 (a), Ti-alloy (b), PEEK (c), MS Si3N4 (d), GPS Si3N4 (e), and HPS Si3N4 (f) were 68 ± 10, 35 ± 7, 79 ± 13, 14 ± 5, 21 ± 5, and 25 ± 4, respectively. The bacterial count of the GPS Si3N4, HPS Si3N4 and MS Si3N4 group is much smaller than that of PEEK and Al2O3, and slightly smaller than that of Ti-alloy. This indicated the antibacterial activity of Si3N4 prepared by three sintering processes against E. coli is stronger than the other three control samples. Among the three sintering processes, MS Si3N4 has the strongest antibacterial activity.

Comparison of antibacterial properties between 3D printed Si3N4 samples with different sintering method on S. Aureus and E. coli. Displayed the E. coli colony plates of Si3N4 samples prepared by different sintering processes: (a) Al2O3; (b) Ti-alloy; (c) PEEK; (d) MS Si3N4; (e) GPS Si3N4; (f) HPS Si3N4; (g) Bar chart of antibacterial activity of Si3N4 samples prepared by different sintering processes and control samples on E. coli (*P < 0.05). Displayed the colony plates of S. aureus prepared by different sintering processes for Si3N4 samples: (A) Al2O3; (B) Ti-alloy; (C) PEEK; (D) MS Si3N4; (E) GPS Si3N4; (F) HPS Si3N4; (G) Bar chart of antibacterial activity of Si3N4 samples prepared by different sintering processes and control samples on S. aureus (*P < 0.05).

The antibacterial effect of Si3N4 samples prepared by different sintering processes and control samples on S. aureus is shown in Fig. 5A–G. It can be clearly seen that the bacterial count of the Si3N4 group sintered by GPS, HPS, and MS is much smaller than that of Al2O3, Ti-alloy, and PEEK, and PEEK has the highest residual bacterial count. The bacterial count of corresponding flat plates for Al2O3 (A), Ti-alloy (B), PEEK (C), MS Si3N4 (D), GPS Si3N4 (E), and HPS Si3N4 (F) were 49 ± 9, 55 ± 8, 67 ± 11, 7 ± 5, 10 ± 6, and 13 ± 8, respectively. The bacterial count of the GPS Si3N4, HPS Si3N4, and MS Si3N4 group is much smaller than that of Al2O3, Ti-alloy, and PEEK. The antibacterial activity of Si3N4 samples prepared by three sintering processes against S. aureus is stronger than the other three control samples. Among the three sintering processes, MS Si3N4 has the strongest antibacterial activity.

The cell adhesion on different materials is shown in Fig. 6. As shown in Fig. 6, cells can adhere to various materials and exhibit a patchy distribution on all materials. In the electron microscope, the adhesion morphology of cells changes due to the surface morphology of the material. From Fig. 6a–c, on the surfaces of the three types of Si3N4, cells mainly adhere to the materials in spindle or divergent shapes. At the same time, filamentous pseudopodia extending from the cell edge to the material surface can be observed. Among them, the cells on the MS sample adhered tightly and maintained good morphology, followed by the GPS sample, which adhered tightly but had weak morphology, and the HPS sample had poor adhesion and dispersed morphology. From Fig. 6d–f, the adhesion of cells on PEEK, Al2O3, and Ti-alloy is different from that on Si3N4. Due to the influence of surface morphology and material, the cells cannot maintain their original morphology, which has a certain impact on their adsorption, migration, and reproduction.

Cell adhesion of different materials: (a) MS Si3N4; (b) GPS Si3N4; (c) HPS Si3N4; (d) PEEK; (e) Al2O3; (f) Ti-alloy. (Red arrow: cell).

Stain the cells on the material using Actin-Tracker Red-Rhodamine and DAPI, and observe with CLSM, as shown in Fig. 7. It can be observed that the cell skeletons on the surfaces of the three Si3N4 materials all exhibit divergent or spindle like shapes, but their specific shapes, quantities, and sizes vary to some extent. The cell skeleton morphology on the MS samples is the best. In addition, the cells on the three types of Si3N4 are cross-linked with each other, and the red microfilament proteins of each cell bind to each other. The cell skeletons on PEEK, Al2O3, and Ti-alloys exhibit varying sizes, slightly fewer quantities, and irregular shapes. From the number of blue circular spots and red microfilament protein connections on each sample, it can be inferred that the number or degree of cell connections in the three types of control materials are weaker than those in the three types of Si3N4 materials.

Morphology of Si3N4 cell cytoskeleton on different material surfaces: (a) MS Si3N4; (b) GPS Si3N4; (c) HPS Si3N4; (d) PEEK; (e) Al2O3; (f) Ti-alloy. (Green arrow: nucleus, yellow arrow: actin filament).

Si3N4 material is the “king of comprehensive performance” in inorganic materials, with excellent comprehensive performance and great application prospects in many fields36. However, Si3N4 material has the characteristics of high sintering temperature and difficult sintering density32,37. When the sintering temperature exceeds 1600 °C, the higher the temperature, the more severe its volatilization and decomposition32. Even with high nitrogen pressure, the high-temperature decomposition of Si3N4 material cannot be avoided, Traditional sintered Si3N4 materials generally adopt the method of HPS to apply greater mechanical pressure to promote the dense sintering of Si3N4, or adopt the method of GPS to add more liquid phase sintering additives to promote the dense sintering of Si3N438. In the HPS method, due to the special nature of mechanical pressure applied from top to bottom, only flat and simple products can be prepared, which has significant limitations on the shape of the products and is not suitable for sintering complex shaped products 39. In the GPS method, in order to achieve high density, more liquid phase sintering aids are added or the sintering temperature is increased to improve the sintering ability of the liquid phase, which promotes the ability of α-Si3N4 converted into β-Si3N4 phase. It leads to the presence of a more obvious glassy second phase substance at the grain boundaries of Si3N4 sintered body, which has a certain effect on the mechanical performance of the material40. Moreover, traditional sintering equipment such as GPS furnaces and HPS furnaces have heating elements, fixtures, carriers, insulation layers, etc. made of graphite or carbon materials. At high temperatures, there is a large amount of carbon thermal reduction atmosphere in the sintering chamber that is not controlled, resulting in chaotic and turbulent sintering atmosphere. Moreover, at high temperatures, the carbon thermal reduction atmosphere is prone to interface reaction with Si3N4 materials, generating silicon carbide (SiC) and nitrogen, causing corrosion and infiltration on the surface of Si3N4 material, resulting in the decrease in material properties41. Therefore, traditional sintering methods such as GPS and HPS have the significant effect on the sintering properties of Si3N4 materials due to the unstable sintering environment. In addition, due to the fact that both HPS and GPS belong to external heating, the heating element heats up the Si3N4 material sample through thermal conduction or radiation. Therefore, there exists a local process of heating first and then gradually from the outside to the inside, which not only makes the degreasing process long-time, has multiple procedures, and has a high probability of defects, but also leads to inconsistent and uneven time for the liquid phase generation of internal sintering aids, resulting in irregular crystal structure growth under the action of the liquid phase during the Si3N4 crystal phase transformation process, which has the significant effect on material performance42,43.

In this research, compared with GPS Si3N4 and HPS Si3N4, MS Si3N4 have ideal microstructure and excellent mechanical properties, which are closely related to the characteristics of MS. MS is a green sintering technology that relies on the material itself to absorb microwave energy at high-frequency microwave frequencies to achieve self-heating and heating25,28. In this research, four 1.5 kW 2.45 GHz microwave sources were used in the microwave sintering equipment, which were uniformly arranged in a three-dimensional manner. At the same time, the insulation barrel inside the microwave cavity always maintained a clockwise rotation state of 60 revolutions per minute. Therefore, under the combined effect of microwave uniform radiation and effective diffuse reflection, uniform heating of the material was achieved, which is conducive to achieving the same frequency resonance of the material itself and completing high-quality degreasing and the sintering densification process quickly and effectively, beneficial for high-quality growth and complete growth of silicon nitride crystals, and beneficial for improving material properties44. In terms of microwave sintering structure, due to the selective heating characteristics of microwaves, the research used recrystallized SiC material as an auxiliary heating plate and constructed a microwave hybrid heating technology sintering structure. By utilizing the excellent microwave absorption performance of recrystallized SiC materials at low temperatures and the effective absorption of microwaves by organic binders (The thermal decomposition carbon products of PE and PW) in the 3D printed bodies, effective and uniform auxiliary heating was carried out when the absorption performance of Si3N4 materials was poor at lower temperatures25. After the sintering temperature reached 600 °C, the absorption performance of Si3N4 material was significantly improved. At this time, utilizing the characteristic of relatively small changes in the absorption performance of recrystallized SiC materials at high and low temperatures, the absorption performance of recrystallized SiC material is still at the original level at high temperatures. Therefore, the main body that absorbs microwave energy gradually realizes the transformation from recrystallized SiC materials to Si3N4 materials45. Finally, the densification sintering of Si3N4 materials is mainly achieved through the absorption of microwave energy by the Si3N4 materials themselves.

At the 2.45 GHz high-frequency microwave frequency, the sintering activity of Si3N4 material was significantly improved, the liquid phase generation temperature was significantly reduced, the dense sintering temperature of Si3N4 material was significantly reduced, and the high-temperature decomposition and volatilization of Si3N4 were effectively suppressed. Therefore, in this study, microwave sintering of dense silicon nitride materials was achieved at only 1620 °C and did not require gas pressure or mechanical pressure to promote densification sintering. Compared with the HPS temperature of 1650 °C and the GPS temperature of 1700 °C, the phenomenon of volatilization and decomposition of samples during microwave sintering is significantly reduced. The overall self-heating method of Si3N4 material effectively ensures the high uniformity of material heating, the uniform removal of organic binders, the uniform generation of liquid phase, and the uniform transformation of Si3N4 crystal phase42. During the crystal phase transformation, the improvement of the uniform liquid phase effect allows the Si3N4 crystal to grow fully, forming a more perfect and ideal Si3N4 crystal structure with longer diameter, and the comprehensive mechanical performance of Si3N4 material has been significantly improved46. In addition, due to the special structure of microwave equipment, high-temperature volatiles are cooled and adhered to the water-cooled furnace wall after coming out of the insulation barrel, completely isolated from the high-temperature sintering area. The high-temperature sintering area is surrounded by insulation barrels layer by layer, and the temperature outside the insulation barrel is about 60–80 °C. The distance between the insulation barrel and the metal water-cooled furnace wall is more than 50 cm, and the temperature of the metal water-cooled furnace wall is around 20 °C under normal pressure, The high-temperature volatile atmosphere will not affect the sintering atmosphere in the high-temperature sintering zone, and there is no graphite or carbon material in the MS structure, so there will be no carbon reduction atmosphere in the GPS and HPS, thereby ensuring a pure atmosphere in the high-temperature sintering zone. It has significant gain impact on the high-quality sintering of silicon nitride materials and the ideal growth of Si3N4 crystals, thereby achieving excellent mechanical properties. This is also the main reason why MS Si3N4 materials have significant advantages in biocompatibility, cytotoxicity testing, evaluation of antibacterial properties, and comparison of cell adhesion and morphology.

Due to the decrease in liquid phase generation temperature of Si3N4 materials in microwave environments, the densification and sintering temperature of Si3N4 materials can be significantly reduced47. Low temperature sintering of dense Si3N4 materials with small grains helps to increase the comprehensive mechanical performance of Si3N4 materials48. From the appearance after sintering, it can be seen that the sample sintered by microwave is not affected by the carbon atmosphere, and the color is significantly lighter. From the microscopic morphology, the micro grain boundaries of the sample sintered by microwave are clean. This is because during the sintering process, the Si3N4 body reaches the liquid phase temperature and forms a glassy phase on the Si3N4 grain boundaries. After effectively assisting in the sintering of Si3N4 materials, it still has the characteristic of microwave selective heating, The liquid sintering aid continues to absorb a large amount of microwave energy, gradually evaporating and purifying, and finally obtaining a dense material of Si3N4 with clean grain boundaries49,50. The schematic diagram of MS principle is shown in Fig. 8a–f. At different stages of MS, the degree to which samples absorb microwaves varies. At low temperatures, Si3N4 materials absorb less microwaves and rely on auxiliary heating materials to absorb microwaves to increase temperature. Auxiliary heating materials include recrystallized SiC materials and organic binders (The thermal decomposition carbon products of PE and PW)25. After reaching a certain temperature, especially after the liquid phase appears, the microwave absorption ability of Si3N4 materials is greatly improved, while the microwave absorption ability of auxiliary heating material SiC is relatively reduced, and the microwave energy is concentrated in the Si3N4 material itself. In the later stage of sintering, the liquid phase gradually decreases, and the absorption ability of silicon nitride materials decreases. At the same time, Si3N4 materials gradually complete dense sintering. The dense sintering mechanism of Si3N4 is a process of transformation from α phase to β phase51, which is achieved in the liquid phase. At a certain temperature, due to the action of additives, a liquid phase is generated that is close to the Si3N4 crystal52. The Si3N4 crystal phase dissolves and precipitates in the liquid phase, completing the transformation and densification process of the Si3N4 crystal phase3. At the same time, the liquid phase slowly evaporates, and the spacing between crystals decreases53. The ideal state is complete evaporation of the liquid phase, Si3N4 crystals are tightly bound in a directional manner, with pure and impurity free phases at grain boundaries, accompanied by significant macroscopic volume shrinkage54. Due to different sintering methods, harsh atmosphere and inconsistent temperature uniformity, the additive effect is poor, the densification process is not ideal, the crystal growth is incomplete, the crystal growth direction is disordered, and finally the Si3N4 crystals cannot be perfectly tightly combined, which has significant negative effect on the material properties7,55. The columnar crystals of β-Si3N4 are the main reason for the high mechanical properties of Si3N4 materials, so the diameter of crystals, aspect ratio, and the integrity of crystal growth, are important factors determining whether Si3N4 materials can have high mechanical properties56. Among them, the aspect ratio and directionality of the crystal are more critical57. From the experimental results of this study, it can be seen that compared to GPS Si3N4 and HPS Si3N4, MS Si3N4 yields a suitable diameter size of the columnar crystal achieves high mechanical properties due to its high aspect ratio, intact crystal morphology, and directionality.

Schematic diagram of the principle of microwave sintering 3D printing of Si3N4 material: (a) Si3N4 particles and sintering additives are 3D printed into a green body, which is then placed in a microwave sintering furnace for degreasing in the air. The SiC substrate absorbs microwave energy to assist in heating the Si3N4 green body; (b) The microwave radiation heating of Si3N4 green body decomposes organic matter into carbon products to assist in heating Si3N4 green body, and gradually oxidizes and removes it in the air; (c) As the temperature continues to rise, the microwave absorption capacity of Si3N4 material significantly increases, while the microwave absorption capacity of SiC substrate relatively decreases; (d) When the temperature reaches a certain level, a sintering additive liquid phase is generated, which slowly wets the Si3N4 particles and further enhances the overall microwave absorption ability of the Si3N4 body; (e) The liquid phase effect of the additive is enhanced, gradually enveloping the Si3N4 particles. The Si3N4 crystal phase begins to transform, and the ability of the SiC substrate to absorb microwaves is further reduced; (f) Si3N4 gradually undergoes phase transition under the action of liquid phase, forming a columnar shape β-Si3N4 crystal. The distance between crystals decreases, and the liquid phase slowly evaporates, resulting in a significant reduction in the volume of the material. The material gradually becomes dense and its ability to absorb microwave energy decreases.

This study successfully prepared 3D printed dense Si3N4 material using a newly constructed microwave heating structure. At present, the mechanical performance and biological activity of Si3N4 materials aim to test whether the basic properties of microwave sintered 3D printed Si3N4 materials as bone replacement materials meet the basic requirements of applications. Compared with Alumina, Titanium alloy, PEEK, GPS Si3N4 and HPS Si3N4, the 3D printed Si3N4 bioceramics sintered by microwave have the best mechanical performance: bending strength is 928 MPa, fracture toughness is 9.61 MPa·m1/2, vickers hardness is 16.2 GPa, compressive strength is 3215 MPa. Meanwhile, it has excellent biocompatibility and antibacterial properties, and the activity of cells on its surface is excellent. Due to the special microwave sintering effect, a large amount of organic matter in 3D printed Si3N4 bodies can be efficiently and high-quality removed, the β-Si3N4crystal growth is more complete, the crystal diameter is smaller, and the crystal aspect ratio is larger, significantly improving the mechanical properties and vitro biological activity of Si3N4 materials. Microwave-sintered 3D-printed Si3N4 bioceramics have significant properties advantages and are an excellent and promising substitute material for implants. This research provides a feasible preparation program for the customization and high reliability performance of silicon nitride bioceramic. Such results should provide better clinical outcomes, improve the patient's medical experience and quality of life.

All data generated or analysed during this study are included in this published article.

Howlett, C. R., McCartney, E. & Ching, W. The effect of silicon nitride ceramic on rabbit skeletal cells and tissue. Clin. Orthop. Relat. Res. 224, 293–304 (1989).

Google Scholar

Cecen, B. et al. Biocompatibility of silicon nitride produced via partial sintering & tape casting. Ceram. Int. 47(3), 3938–3945 (2021).

Article MathSciNet CAS Google Scholar

Pezzotti, G. et al. Mechanisms of instantaneous inactivation of SARS-CoV-2 by silicon nitride bioceramic. Mater. Today BioSep. 12, 100144 (2021).

Article CAS Google Scholar

Strasser, V. & Sikirić, M. D. Bone regeneration with ceramics scaffold. Encycl. Mater. Tech. Ceram. Glasses 3, 646–661 (2021).

Article Google Scholar

Bal, B. S. & Rahaman, M. N. Orthopedic applications of silicon nitride ceramics. Acta Biomater. 8(8), 2889–2898 (2012).

Article CAS PubMed Google Scholar

Neumann, A. et al. Comparative investigation of the biocompatibility of various silicon nitride ceramic qualities in vitro. J. Mater. Sci. Mater. Med. 15(10), 1135–1140 (2004).

Article CAS PubMed Google Scholar

Wu, H. et al. Enhanced bacteriostatic activity, osteogenesis and osseointegration of silicon nitride/polyetherketoneketone composites with femtosecond laser induced micro/nano structural surface. Appl. Mater. Today 18, 100523 (2020).

Article Google Scholar

Neumann, A. et al. Prototype of a silicon nitride ceramic-based miniplate osteofixation system for the midface. Otolaryngol. Head Neck Surg. 134(6), 923–930 (2006).

Article PubMed Google Scholar

Zeng, X. F. et al. Fabrication of 3D printed Si3N4 bioceramics with superior comprehensive performance through ZnO nanowires doping. Ceram. Int. https://doi.org/10.1016/j.ceramint.2024.06.156 (2024).

Article Google Scholar

Raza, S. M., Khurshid, Z., Zafar, M. S., Najeeb, S. & Yaqin, S. A. U. S.A.U. 15-Silicon Nitride (SiN): An Emerging Material for Dental Implant Applications. In Dental Implants 287–299 (Elsevier, 2020). https://doi.org/10.1016/B978-0-12-819586-4.00015-9.

Chapter Google Scholar

Punj, S., Singh, J. & Singh, K. Ceramic biomaterials: properties, state of the art and future prospectives. Ceram. Int. 47(20), 28059–28074 (2021).

Article CAS Google Scholar

Zeng, X. F. et al. Mechanical properties and biological activity of 3D printed silicon nitride materials. Ceram. Int. 50(9), 16704–16713 (2024).

Article CAS Google Scholar

Boschetto, F. et al. In situ molecular vibration insights into the antibacterial behavior of silicon nitride bioceramic versus gram-negative Escherichia coli. Spectrochim Acta Part A 223, 117299 (2019).

Article CAS Google Scholar

Grippi, T. et al. Grain growth modeling for gas pressure sintering of silicon nitride based ceramics. Mater. Today Commun. 34, 105189 (2023).

Article CAS Google Scholar

Feng, H. et al. Elimination of grain boundaries and its effect on the properties of silicon nitride ceramics. Ceram. Int. 46(8), 12606–12612 (2020).

Article Google Scholar

He, Q. et al. Additive manufacturing of dense zirconia ceramics by fused deposition modeling via screw extrusion. J. Eur. Ceram. Soc. 41(1), 1033–1040 (2021).

Article CAS Google Scholar

Cano, S. et al. Additive manufacturing of zirconia parts by fused filament fabrication and solvent debinding: Selection of binder formulation. Addit. Manuf. 26(3), 117–128 (2019).

CAS Google Scholar

Gorjan, L., Tonello, R., Sebastian, T., Colombo, P. & Clemens, F. Fused deposition modeling of mullite structures from a preceramic polymer and gamma-alumina. J. Eur. Ceram. Soc. 39(7), 2463–2471 (2019).

Article CAS Google Scholar

Arnesano, A., Sanosh, K. P., Notarangelo, A., Montagna, F. & Licciulli, A. Fused deposition modeling shaping of glass infiltrated alumina for dental restoration. Ceram. Int. 46(2), 2206–2212 (2020).

Article CAS Google Scholar

Budharaju, H. et al. Ceramic materials for 3D printing of biomimetic bone scaffolds—Current state-of-the-art & future perspectives. Mater. Des. 231, 112064 (2023).

Article CAS Google Scholar

Zou, R. et al. A biocompatible silicon nitride dental implant material prepared by digital light processing technology. J. Mech. Behav. Biomed. Mater. 141, 105756 (2023).

Article CAS PubMed Google Scholar

Ly, M., Spinelli, S., Hays, S. & Zhu, D. 3D printing of ceramic biomaterials. Eng. Regener. 3, 41–52 (2022).

Google Scholar

Zhao, J. et al. Digital light processing of high-strength Si3N4 ceramic: Role of particle grading on slurries curing and mechanical properties. Ceram. Int. 50(13), 22722–22732 (2024).

Article CAS Google Scholar

Zeng, X. F., Qian, D. F., Peng, H., Li, W. F. & Liu, X. Y. Influence of microwave sintering environment on the preparation of AlN powder and ceramic. Key Eng. Mater. 368–372, 967–969 (2008).

Article Google Scholar

Zeng, X. F. et al. Effects of additive on the microwave synthesis of AlN powder. J. Am. Ceram. Soc. 90(10), 3289–3292 (2007).

Article CAS Google Scholar

He, J. Y. et al. Silicon nitride bioceramics sintered by microwave exhibit excellent mechanical properties, cytocompatibility in vitro, and anti-bacterial properties. J. Funct. Biomater. 14, 552 (2023).

Article CAS PubMed PubMed Central Google Scholar

Swapna, Y. V., Mathew, C. T. & Thomas, J. K. Resistive coupled microwave sintering of hydroxyapatite/titania nano-biocomposite and tailoring its mechanical properties. J. Mech. Behav. Biomed. Mater. 141, 105772 (2023).

Article CAS PubMed Google Scholar

Abbas, M. K. G., Ramesh, S., Tasfy, S. F. H. & Sara Lee, K. Y. Effect of microwave sintering on the properties of copper oxide doped alumina toughened zirconia (ATZ). J. Mater. Res. Tech. 25, 1041–1054 (2023).

Article CAS Google Scholar

Khalile, N., Petit, C., Meunier, C. & Valdivieso, F. Hybrid microwave sintering of zirconia toughened alumina in a multimode cavity—Influence of the content of 3 mol% yttria stabilized zirconia and sintering configurations. Open Ceram. 14, 100371 (2023).

Article CAS Google Scholar

Goulas, A. et al. Multi-material additive manufacture and microwave-assisted sintering of a metal/ceramic metamaterial antenna structure. Appl. Mater. Today 33, 101878 (2023).

Article Google Scholar

Xiao, C. & Han, B. Preparation of porous silicon nitride ceramics by microwave sintering and its performance evaluation. J. Mater. Res. Tech. 8(6), 5984–5995 (2019).

Article Google Scholar

Liu, Y. et al. Effect of the ratio of Y2O3 and MgSiN2 sintering additives on the microstructure, thermal and mechanical properties of Si3N4 ceramics. Ceram. Int. 49(22), 36490–36496 (2023).

Article CAS Google Scholar

Wang, W. D. et al. Effect of in-situ formed Y2O3 by metal hydride reduction reaction on thermal conductivity of β-Si3N4 ceramics. J. Eur. Ceram. Soc. 40(15), 5316–5323 (2020).

Article CAS Google Scholar

Fu, S. et al. Effects of Gd2O3 and MgSiN2 sintering additives on the thermal conductivity and mechanical properties of Si3N4 ceramics. J. Appl. Ceram. Tech. 20(3), 1855–1864 (2023).

Article CAS Google Scholar

Li, S. S. et al. Effects of Y2O3/MgO ratio on mechanical properties and thermal conductivity of silicon nitride ceramics. J. Appl. Ceram. Tech. 19(5), 2873–2882 (2022).

MathSciNet CAS Google Scholar

Manghnani, S., Shekhawat, D., Goswami, C., Patnaik, T. K. & Singh, T. Mechanical and tribological characteristics of Si3N4 reinforced aluminium matrix composites: A short review. Mater. Today: Proc. 44(6), 4059–4064 (2021).

CAS Google Scholar

Grigoriev, S. N., Hamdy, K., Volosova, M. A., Okunkova, A. A. & Fedorov, S. V. Electrical discharge machining of oxide and nitride ceramics: A review. Mater. Des. 209, 109965 (2021).

Article CAS Google Scholar

Yin, S. et al. Preparation, mechanical and thermal properties of Si3N4 ceramics by gelcasting using low-toxic DMAA gelling system and gas pressure sintering. Ceram. Int. 44(18), 22412–22420 (2018).

Article CAS Google Scholar

Kumar, K. et al. Twofold increase in Weibull modulus of hot-pressed Si3N4 ceramic by modified pressing profile. Mater. Today Commun. 32, 103979 (2022).

Article CAS Google Scholar

Hu, J. B. et al. Fabrication of Si3N4 ceramics with high thermal conductivity and flexural strength via novel two-step gas-pressure sintering. J. Eur. Ceram. Soc. 42(12), 4846–4854 (2022).

Article CAS Google Scholar

Jana, P., Dietrich, S. & Roy, S. Effect of SiC particle size on the strength and stiffness of porous Si3N4-SiC composites fabricated via a low-temperature sintering process. Mater. Sci. Eng. A 864, 144614 (2023).

Article Google Scholar

Ye, C. C., Wei, W. Q., Fu, X., Wang, C. H. & Ru, H. Q. Effect of sintering activation energy on Si3N4 composite ceramics. Ceram. Int. 48(4), 4851–4857 (2022).

Article CAS Google Scholar

Bai, L., Mao, X. D., Shen, W. P. & Ge, C. C. Comparative study of β-Si3N4 powders prepared by SHS sintered by spark plasma sintering and hot pressing. J. Univ. Sci. Tech. Beijing Miner. Metall. Mater. 14(3), 271–275 (2007).

CAS Google Scholar

Zhang, Y. Q. et al. Preparation of novel Ti–Y/ZrO2 ceramic by two-step of mechanical alloying and microwave-assisted sintering process. J. Mater. Res. Tech. 27, 3436–3446 (2023).

Article CAS Google Scholar

Qi, Y. S. et al. nvestigation on the microwave sintering heating process and mechanism of h-BN/ZrO2/SiC composites. Ceram. Int. 49(2), 20594–20600 (2023).

Article CAS Google Scholar

Qin, Q. et al. Preparation of SiC nanowires based on graphene as the template by microwave sintering. J. Alloys. Compd. 910, 164746 (2022).

Article CAS Google Scholar

Xu, W. W., Yin, Z. B., Yuan, J. T. & Yan, G. D. Reliability prediction of a microwave sintered Si3N4-based composite ceramic tool. Ceram. Int. 47(12), 16737–16745 (2021).

Article CAS Google Scholar

Guo, C., Ye, F. & Cheng, L. In situ growth of single crystal Si3N4 nanowire foam with good wave-transparency and heat insulation performance. Compos. Part B 224, 109129 (2021).

Article CAS Google Scholar

Aiyi, P., Li, J. G., Chen, Y., Li, M. J. & Shen, Q. Low-temperature fabrication of Si3N4 ceramics with high thermal conductivities using a single Mg2Si sintering additive. Ceram. Int. 49(23), 39473–39478 (2023).

Article Google Scholar

Suri, J. & Shaw, L. Liquid phase sintering of Si3N4/SiC nanopowders derived from silica fume. Ceram. Int. 40(7), 9179–9187 (2014).

Article CAS Google Scholar

Bocanegra-Bernal, M. H. & Matovic, B. Mechanical properties of silicon nitride-based ceramics and its use in structural applications at high temperatures. Mater. Sci. Eng. A 527(6), 1314–1338 (2010).

Article Google Scholar

Cao, L., Wang, Z., Yin, Z., Liu, K. & Yuan, J. Investigation on mechanical properties and microstructure of silicon nitride ceramics fabricated by spark plasma sintering. Mater. Sci. Eng. A 731, 595–602 (2018).

Article CAS Google Scholar

Gan, Z., Wang, C. & Chen, Z. Material structure and mechanical properties of silicon nitride and silicon oxynitride thin films deposited by plasma enhanced chemical vapor deposition. Surface 1, 59–72 (2018).

Article Google Scholar

Imamura, H., Hirao, K., Brito, M. E., Toriyama, M. & Kanzaki, S. Further improvement in mechanical properties of highly anisotropic silicon nitride ceramics. J. Am. Ceram. Soc. 83(3), 495–500 (2000).

Article CAS Google Scholar

Kawaoka, H. et al. Effect of α/β phase ratio on microstructure and mechanical properties of silicon nitride ceramics. J. Mater. Res. 16(8), 2264–2270 (2011).

Article ADS Google Scholar

Yin, Y. J., Yan, K., Chen, F., Zhu, Y. S. & Hong, J. Tribological properties of graphene/β-Si3N4 whisker reinforced Si3N4 ceramic composites. Ceram. Int. 49(23), 37568–37575 (2023).

Article CAS Google Scholar

Huang, J. W., Lv, X. A., Dong, X. F., Hussain, M. I. & Ge, C. C. Microstructure and mechanical properties of α/β-Si3N4 composite ceramics with novel ternary additives prepared via spark plasma sintering. Ceram. Int. 48(20), 30376–30383 (2022).

Article CAS Google Scholar

Download references

The authors acknowledge Faculty of Engineering, University Malaysia Sabah for their support and assistance in this research work. The authors acknowledge Prof. Coswald’s group for their guidance with the experimental setup and lab work. The authors also acknowledge Power and Energy Research Laboratories (PERL) Group of University of Malaysia Sabah for their guidance.

Faculty of Engineering, University Malaysia Sabah, 88400, Kota Kinabalu, Sabah, Malaysia

Xiaofeng Zeng, Coswald Stephen Sipaut, Noor Maizura Ismail & Yan yan Farm

Hengyang Kaixin Special Material Technology Co., Ltd., Hengyang, 421200, China

Xiaofeng Zeng & Bo Peng

School of Minerals Processing and Bioengineering, Central South University, Changsha, 410083, China

Yuandong Liu & Jiayu He

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

Zeng Xiaofeng: Conceptualization, Methodology, Validation, Writing-Original Draft. Coswald Stephen Sipaut: Supervision, Project Administration. Noor Maizura Ismail: Data Curation, Visualization, Supervision, Investigation, Writing - Review & Editing. Yuandong Liu: Supervision, Investigation, Formal Analysis. Yan yan Farm: Supervision, Methodology, Validation. Bo Peng：Data Curation, Writing - Review & Editing. Jiayu He: Resources, Data Curation, Visualization. All authors reviewed the manuscript.

Correspondence to Xiaofeng Zeng or Yan yan Farm.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary Video 1.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and permissions

Zeng, X., Sipaut, C.S., Ismail, N.M. et al. Preparation of 3D printed silicon nitride bioceramics by microwave sintering. Sci Rep 14, 15825 (2024). https://doi.org/10.1038/s41598-024-66942-w

Download citation

Received: 07 May 2024

Accepted: 05 July 2024

Published: 09 July 2024

DOI: https://doi.org/10.1038/s41598-024-66942-w

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative